GRCop-42 Development and Hot-fire Testing Using Additive Manufacturing Powder Bed Fusion for Channel-Cooled Combustion Chambers

[摘要] GRCop-42 is a high conductivity, high-strength dispersion strengthened copper-alloy for use in high heat flux applications such as liquid rocket engine combustion devices. This alloy is part of the family of NASA-developed GRCop, copper-chrome-niobium alloys. GRCop alloys were developed for harsh environments specific to regeneratively-cooled combustion chambers and nozzles with good oxidation resistance. Significant development was completed on the GRCop-84 and GRCop-42 alloys in the extruded wrought form demonstrating feasibility for combustion chambers. NASA has recently developed a process for additive manufacturing, specifically Powder Bed Fusion (PBF) or Selective Laser Melting (SLM), of GRCop-42 to establish parameters, characterize the material, and complete testing of components with complex internal features. This evolution of the GRCop-42 was based on the successful predecessor development work using GRCop-84 with the motivation of establishing a new copper-alloy option for use in NASA, government, and industry programs with SLM. A few advantages have been shown with the GRCop-42 that include higher conductivity and faster build speeds over the GRCop-84, and a simplified powder supply chain. Initial property development has shown that it is possible to produce high density builds with strengths equivalent to wrought GRCop-42 and a conductivity greater than GRCop-84. The GRCop-42 has completed process development and initial properties have been established. Several demonstrator combustion chambers have also been fabricated with the SLM GRCop-42 that include integral channels and closeouts. Additional test units have been fabricated and are completing substantial hot-fire testing to demonstrate performance of the material, process, and design.

[发布日期] 2019-08-16

[学科分类] 金属与冶金

[关键词] ADDITIVE MANUFACTURING;COMBUSTION CHAMBERS;COPPER ALLOYS;DISPERSION STRENGTHENING;FUSION (MELTING);LIQUID PROPELLANT ROCKET ENGINES;NIOBIUM ALLOYS;PERFORMANCE TESTS;POWDER (PARTICLES);RAPID PROTOTYPING;WROUGHT ALLOYS