Crystallization Behavior of M97 Series Silicone Cushions

[摘要] M97 series siloxanes are poly(dimethyl-diphenyl) siloxanes that are reinforced through a mixture of precipitated and fumed silica fillers which are blended in through the addition of a short chain polydimethylsiloxane processing aid. M97 silicones exhibit crystallization at -80.25 C by thermal (modulated differential scanning calorimetry) and mechanical (dynamic mechanical analysis) techniques. Isothermal dynamic mechanical analysis experiments illustrated that crystallization occurred over a 1.8 hour period in silica-filled systems and 2.8 hours in unfilled systems. The onset of crystallization typically occurred after a 30 minute incubation/nucleation period. {gamma}-radiation caused the crystallization rate to decrease proportionally with dosage, but did not decrease the amount of crystallization that ultimately occurred. Irradiation in vacuum resulted in slower overall crystallization rates compared to air irradiation due to increased crosslinking of the polymer matrix under vacuum. Modulated differential scanning calorimetry contrasted the crystallization and melting behavior of pure PDMS versus the M97 base polymer and helped determine which component of the composite was the origin of the crystallization phenomena.

[发布日期] 2000-09-07 [发布机构] Lawrence Livermore National Laboratory

[关键词] Calorimetry;Mixtures;Irradiation;Origin;Air