Microstructural examination of commercial ferritic alloys at 200 dpa

[摘要] Microstructures and density change measurements are reported for martensitic commercial steels HT-9 and modified 9Cr-1Mo (T91) and oxide dispersion strengthened ferritic alloys MA956 and MA957 following irradiation in the FFTF/MOTA at 420 degrees C to 200 dpa. Swelling as determined by density change remains below 2% for all conditions. Microstructures are found to be stable except in recrystallized grains of MA957, which are fabrication artifacts, with only minor swelling in the martensitic steels and alpha' precipitation in alloys with 12% or more chromium. These results further demonstrate the high swelling resistance and microstructural stability of the ferritic alloy class.

[发布日期] 1996-10-01

[效力级别]  Proceedings Paper