Revision of the tensile database for V-Ti and V-Cr-Ti alloys tested at ANL

[摘要] The database for the tensile properties of unirradiated and irradiated V-(0-18) wt%Ti and V-(4-15) wt%Cr-(3-15) wt%Ti alloys tested at Argonne National Laboratory (ANL) has been reviewed and, when necessary, revised. A consistent methodology, based on ASTM terminology and standards, has been used to reanalyze the unpublished load vs. displacement curves for 162 unirradiated samples and 91 irradiated samples to determine revised values for yield strength (YS), ultimate tensile strength (UTS), uniform elongation (UE), and total elongation (TE). The revised values for UE and TE are lower by 5 +/- 2% (strain) and 4 +/- 2% (strain), respectively, than previously reported values, which included displacements due to machine compliance. Revised values for YS and UTS are consistent with previously published values in that they are within the scatter usually associated with these properties. (C) 1998 Elsevier Science B.V. All rights reserved.