Helium retention and surface morphology of oxidized vanadium alloy

[摘要] The effects of the surface oxidation on the helium desorption and retention behaviors of vanadium alloy were investigated. V-4Cr-4Ti alloy, which was thermally oxidized at 873 K for 15 min with 0.05 Pa, was irradiated by helium ions with energy of 5 key at room temperature. Then, the helium desorption and retention behaviors were evaluated using a technique of thermal desorption spectroscopy. The changes in surface structures by the irradiation were also evaluated. Helium desorption behavior in low temperature region were significantly changed by the oxidation. Helium desorption around 700 K became large for the oxidized sample. The amount of retained helium and the blister size in the oxidized sample were smaller than of those in the non-oxidized one. These results indicate that the surface oxidation significantly affects the helium retention and desorption behaviors of the vanadium alloy. (C) 2010 Elsevier B.V. All rights reserved.

[发布日期] 2011-10-01

[效力级别]  Proceedings Paper