Comparative evaluation of performance of percolated perpendicular media using FePt-MgO/Pt/Cr trilayer and FePt-MgO/MgO bilayer

[摘要] (Fe48Pt52)(100-x)-(MgO)x films were used to examine the performance of a perpendicular percolated medium. Two underlayers, Pt(001)/Cr(002) and MgO(002), were used for comparison. The (Fe48Pt52)(100-x)-(MgO)x film with the MgO underlayer exhibits a strong preference to segregate at FePt grain boundaries. The microstructure with small closely packed MgO particles (2-4nm) dispersed uniformly in the L1(0) FePt matrix was achieved in the Pt/Cr underlayered sample. Structural data reveal that the precipitate is crystallographically coherent with the surrounding L1(0) FePt phase and preserves good lattice alignment. Magnetic results indicate significant pinning behavior for those introduced nonmagnetic columns with an enhanced coercivity of about 70%-much greater than that of the MgO underlayered samples. Percolated perpendicular medium can be realized in the FePt system and a Pt(001)/Cr(002) underlayer promotes the formation of pinning sites within the FePt grains. (C) 2008 Elsevier B. V. All rights reserved.

[发布日期] 2008-11-01

[效力级别]  Proceedings Paper

[关键词] FePt;Percolated perpendicular media;Perpendicular magnetic recording;Underlayer