TRIBOLOGICAL PROPERTIES OF CERAMIC-(TI3AL-NB) SLIDING COUPLES FOR USE AS CANDIDATE SEAL MATERIALS TO 700-DEGREES-C

[摘要] Tribological properties of Ti3Al-Nb intermetallic disks sliding against alumina-boria-silicate fabric were ascertained in air at temperatures from 25 to 700-degrees-C. These materials are candidates for sliding seal applications for the National AeroSpace Plane. The tests were performed using a pin-on-disk tribometer. Sliding was unidirectional at 0.27 m s-1 under a nominal contact stress of 340 kPa. Gold sputter or ion plating deposited films were used to reduce friction and wear. Rhodium and palladium films were used beneath the gold lubicating films to prevent diffusion of the substrate into the gold at high temperature. The friction and wear of the unlubricated specimens were unacceptable. Friction coefficients were generally greater than 1.0. The ion-plated gold films when used with a rhodium diffusion barrier reduced friction by almost a factor of 2. Wear was also substantially reduced. The sputter-deposited films were not adherent unless the substrate was sputter cleaned immediately prior to film deposition. Palladium did not function as a diffusion barrier.

[发布日期] 1990-12-10

[效力级别]  Proceedings Paper