Microstructure and materials properties of understoichiometric TiBx thin films grown by HiPIMS

[摘要] TiBx thin films with a B content of 1.43 <= x <= 2.70 were synthesized using high-power impulse magnetron sputtering (HiPIMS) and direct-current magnetron sputtering (DCMS). HiPIMS allows compositions ranging from understoichiometric to overstoichiometric dense TiBx thin films with a B/Ti ratio between 1.43 and 2.06, while DCMS yields overstoichiometric TiBx films with a B/Ti ratio ranging from 2.20 to 2.70. Excess B in overstoichiometric TiBx thin films from DCMS results in a hardness up to 37.7 +/- 0.8 GPa, attributed to the formation of an amorphous B-rich tissue phase interlacing stoichiometric TiB2 columnar structures. We furthermore show that understoichiometric TiB1.43 thin films synthesized by HiPIMS, where the deficiency of B is found to be accommodated by Ti-rich planar defects, exhibit a superior hardness of 43.9 +/- 0.9 GPa. The apparent fracture toughness and thermal conductivity of understoichiometric TiB1.43 HiPIMS films are 4.2 +/- 0.1 MPa root m and 2.46 +/- 0.22 W/(m.K), respectively, as compared to corresponding values for overstoichiometric TiB2.70 DCMS film samples of 3.1 +/- 0.1 MPa root m and 4.52 +/- 0.45 W/(mK). This work increases the fundamental understanding of understoichiometric TiBx thin films and their materials properties, and shows that understoichiometric films have properties matching or going beyond those with excess B.

[发布日期] 2020-12-25

[关键词] Borides;Stoichiometry;Titanium;Mechanical properties;Microstructure;HiPIMS