High energy density of BaTiO3@TiO2 nanosheet/polymer composites via ping-pong-like electron area scattering and interface engineering

[摘要] Dielectric substances exhibit great potential for high-power capacitors due to their high stability and fast charge–discharge; however, a long-term challenge is to enhance energy density. Here, we propose a poly(vinylidene fluoride) (PVDF) composite utilizing BaTiO3 nanoparticle@TiO2 nanosheet (BT@TO ns) 2D nanohybrids as fillers, aiming at combining the interfacial strategy of using a core–shell filler and the electron scattering of a 2D filler to improve the energy density. With 4 wt% filler, the composite possesses the largest breakdown strength (Eb) of 561.2 MV m−1, which is significantly enhanced from the 407.6 MV m−1 of PVDF, and permittivity of 12.6 at 1 kHz, which is a 23% increase from that of PVDF. A superhigh energy density of 21.3 J cm−3 with an efficiency of 61% is obtained at 550 MV m−1. The 2D BT@TO ns-filled composite exhibits a higher energy density than composites filled with core–shell 1D BT@TO nws or non-core–shell 0D BT, 1D TO, or 2D TO particles. The Eb and energy density improvements are attributed to the buffer layer-based interface engineering and enhanced area scattering of electrons caused by the 2D hybrids, an effect similar to that of a ping-pong paddle to scatter electric field-induced charge migrations in composites. Thus, an effective hybrid strategy is presented for achieving high-performance polymer composites that can be used in energy storage devices.

[发布日期] 2021-12-20