Effect of Environmental Exposures on Fatigue Life of P/M Disk Superalloys

[摘要] As the temperature capability of Ni-base superalloy powder metallurgy disks is steadily increased, environmental resistance and protection of advanced nickel-based turbine disk components are becoming increasingly important. Localized surface hot corrosion attack and damage from oxidation have been shown to impair disk fatigue life and may eventually limit disk operating temperatures. NASA Research Announcement (NRA) contracts have been awarded to GE Aviation and Honeywell Aerospace to separately develop fatigue resistant metallic and ceramic coatings for corrosion resistance and the corrosion/fatigue results of selected coatings will be presented. The microstructural response of a bare ME3 disk superalloy has been evaluated for moderate (704 C) and aggressive (760-816 C) oxidizing exposures up to 2,020 hours. Cross section analysis reveals sub-surface damage (significant for aggressive exposures) that consists of Al2O3 "fingers", interfacial voids, a recrystallized precipitate-free layer and GB carbide dissolution. The effects of a Nichrome corrosion coating on this microstructural response will also be presented.

[发布日期] 2011-05-10

[学科分类] 金属与冶金