SiC Composite Turbine Vanes

[摘要] Turbine inlet guide vanes have been fabricated from composites of silicon carbide fibers in silicon carbide matrices. A unique design for a cloth made from SiC fibers makes it possible to realize the geometric features necessary to form these vanes in the same airfoil shapes as those of prior metal vanes. The fiber component of each of these vanes was made from SiC-fiber cloth coated with boron nitride. The matrix was formed by chemical-vapor infiltration with SiC, then slurry-casting of SiC, followed by melt infiltration with silicon. These SiC/SiC vanes were found to be capable of withstanding temperatures 400 F (222 C) greater than those that can be withstood by nickel-base-superalloy turbine airfoils now in common use in gas turbine engines. The higher temperature capability of SiC/SiC parts is expected to make it possible to use them with significantly less cooling than is used for metallic parts, thereby enabling engines to operate more efficiently while emitting smaller amounts of NOx and CO. The SiC/SiC composite vanes were fabricated in two different configurations. Each vane of one of the configurations has two internal cavities formed by a web between the suction and the pressure sides of the vane. Each vane of the other configuration has no web (see Figure 1). It is difficult to fabricate components having small radii, like those of the trailing edges of these vanes, by use of stiff stoichiometric SiC fibers currently preferred for SiC/SiC composites. To satisfy the severe geometric and structural requirements for these vanes, the aforementioned unique cloth design, denoted by the term Y-cloth, was conceived (see Figure 2). In the regions away from the trailing edge, the Y-cloth features a fiber architecture that had been well characterized and successfully demonstrated in combustor liners. To form a sharp trailing edge (having a radius of 0.3 mm), the cloth was split into two planes during the weaving process. The fiber tows forming the trailing-edge section were interlocked, thereby enhancing through-thickness strength of the resulting composite material. For vanes of the webless configuration, each made from a layup of six plies of Ycloth, the length of each Y-cloth layer was cut so that the two strips corresponding to the aforementioned two planes would wrap around the perimeter of a graphite vane preform tool with a 10-mm overlap. The overlap was used to join the two strips in a fringe splice. To make the external sixth ply, a standard woven cloth was cut to the required final length and a fringe splice joined the two ends of the cloth at the trailing edge. The cloth was then prepregged. The entire assembly was then placed into an aluminum compaction tool designed to form the outer net shape of the vane. After the prepreg material was allowed to dry, the preform was removed from the aluminum tooling and placed into an external graphite tool before being shipped to a vendor for matrix infiltration. To make the SiC fiber preform for a vane having an internal web, a slightly different initial approach was followed. Each of two sections forming the internal cavities (and ultimately the web) was created by first slipping two concentric layers of a two-dimensional, 2-by-2, 45 - braided tube around a net-shape graphite mandrel. The tubes on both mandrels were prepregged and allowed to dry. The resulting two subassemblies were put together, then four additional plies were wrapped around them in the same fashion as that described above for the six plies of the vaneless configuration. The consolidation of the SiC fiber preforms into SiC/SiC composite parts was performed by commercial vendors using their standard processes. The capability of two of the webless SiC/SiC turbine vanes was demonstrated in tests in a turbine environment. The tests included 50 hours of steady-state operation and 102 two-minute thermal cycles. A surface temperature of 1,320 C was reached during the tests.

[发布日期] 2006-10-01

[学科分类] 航空航天科学