Development of Polyimide Foam for Aircraft Sidewall Applications

[摘要] In this paper, the use of polyimide foam as a lining in double panel applications is considered. It is being investigated here as a replacement for aircraft grade glass fiber and has a number of attractive functional attributes, not the least of which is its high fire resistance. The test configuration studied here consisted of two 1mm (0.04 in.) thick, flat aluminum panels separated by 12.7 cm (5.0 in.) with a 7.6 cm (3.0 in.) thick layer of foam centered in that space. Random incidence transmission loss measurements were conducted on this buildup, and conventional poro-elastic models were used to predict the performance of the lining material. Results from two densities of foam are considered. The Biot parameters of the foam were determined by a combination of direct measurement (for density, flow resistivity and Young s modulus) and inverse characterization procedures (for porosity, tortuosity, viscous and thermal characteristic length, Poisson s ratio and loss factor). The inverse characterization procedure involved matching normal incidence standing wave tube measurements of absorption coefficient and transmission loss of the isolated foam with finite element predictions. When the foam parameters determined in this way were used to predict the performance of the complete double panel system, reasonable agreement was obtained between the measured transmission loss and predictions made using a commercial statistical energy analysis code.

[发布日期] 2013-01-07

[学科分类] 复合材料