Diffusivity in Alumina Scales Grown on Al-MAX Phases

[摘要] Ti3AlC2, Ti2AlC, and Cr2AlC are oxidation resistant MAX phase compounds distinguished by the formation of protective Al2O3 scales with well controlled kinetics. A modified Wagner treatment was used to obtain interfacial grain boundary diffusivity, deltaD(sub gb,O,int.), from scale growth rates and corresponding grain size. It is based on the p(O2)(exp -1/6) dependency of the double chargedoxygen vacancy and oxygen diffusivity, coupled with the effective diffusion constant for short circuit grain boundary paths. Data from the literature for MAX phases was analyzed accordingly, and deltaD(sub gb,O,int.) was found to nearly coincide with the Arrhenius line developed for Zr-doped FeCrAl, where: deltaD(sub gb,O,int.) = 1.8x10(exp -10) exp(-375 kJ/RT) cubic meters/s. Furthermore, this oxidation relation suggests the more general format applicable to bulk samples under ambient conditions: deltaD(sub gb,O) = 7.567x10(exp -8) exp(-544 kJ/RT) p(O2)(exp -1/6) cubic meters/[s x Pa(exp -1/6)]. Data from many other FeCrAl(X) studies were similarly assessed to show general agreement with the relation for deltaD(sub gb,O,int.). This analysis reinforces the view that protective alumina scales grow by similar mechanisms for these Al-MAX phases and oxidation resistant FeCrAl alloys.

[发布日期] 2014-08-01

[学科分类] 金属与冶金