A Solid Film Lubricant Composition for Use at High Sliding Velocities in Liquid Nitrogen

[摘要] Solid-lubricant-containing compositions can be of value as films and solid bodies for bearing and seal surfaces in low-temperature liquefied gases. An experimental composition including polytetrafluoroethylene (PTFE), an epoxy resin, and lithium-alumina-silicate was studied in friction, wear, and endurance experiments in liquid nitrogen (-320 F). This composition was formulated to approximate the thermal expansion of metals used in cryogenic systems. Hemisphere (3/6-in. radius) rider specimens were used and in most experiments the load was 1000 g. Films (0.005-in. thick) on disk specimens gave good endurance life, low rider wear, and desirable friction (f = 0.02 to 0.07). They functioned at a higher sliding velocity (no failure at 16, 000 ft/min) with copper rider specimens than with stainless steel riders (failure at 9000 ft/min). Solid rider material of the experimental composition had good friction and wear properties at sliding velocities above 4000 ft/min. It is important to use the experimental composition with mating materials having good thermal conductivity.

[发布日期] 1960-01-01

[学科分类] 材料科学（综合）