Extreme Oxidative Durability of TBCs on Ti2AlC MAX Phases

[摘要] APS and PS-PVD YSZ thermal barrier coatings, applied directly to oxidation resistant Ti2AlC substrates, were oxidized in interrupted furnace tests. Temperature was advanced in 50C intervals from 1100 to 1300C, each 500 h long with eleven cooling cycles. Damage only initiated on the APS coating at 1300C after 15 h, with complete delamination after 500 h. The PS-PVD coating survived all testing. Weight change and metallographic analyses indicate that the YSZ-Ti2AlC systems sustained alumina scale growth of 30-40 m. In comparison, widely used Pt-aluminide bondcoats on single crystal superalloy turbine blades exhibit TBC lives equivalent to alumina scale growth up to 7 m, equivalent to just 200 h at 1200C. It is demonstrated that 25x TBC life improvement (or 180C temperature increase) resulted from the close CTE match of Ti2AlC with those of alumina and YSZ.

[发布日期] 2015-10-04

[学科分类] 金属与冶金