Comparison of Cavitation-Erosion Resistance of Carburized and Carburized-Plus-Nitrided 316LN Stainless Steel in Mercury
[摘要] Annealed type 316LN stainless steel in the (1) carburized and the (2) carburized plus nitrided conditions was evaluated for cavitation-erosion resistance in ambient temperature mercury using a vibratory horn method. The results indicated that, relative to the specimens receiving only the carburizing treatment, the specimens that received both surface treatments exhibited substantially greater weight loss, general thinning, and profile development as a function of sonication time - with all observed degradation limited to the nitrided layer. Further, the nitride layer was observed to be susceptible to extensive cracking (occasionally leading to spallation), but the cracking was never observed to penetrate into the carburized layer. These screening test results suggest there is no improvement in cavitation-erosion resistance associated with augmentation of the carburizing treatment with plasma nitriding.
[发布日期] 2007-05-01 [发布机构] 
[效力级别]  [学科分类] 材料科学(综合)
[关键词] AMBIENT TEMPERATURE;MERCURY;NITRIDES;PLASMA;SPALLATION;STAINLESS STEELS;SURFACE TREATMENTS [时效性] 
   浏览次数:27      统一登录查看全文      激活码登录查看全文