PROBABILITY BASED CORROSION CONTROL FOR WASTE TANKS - PART II

[摘要] As part of an ongoing study to evaluate the discontinuity in the corrosion controls at the SRS tank farm, a study was conducted this year to assess the minimum concentrations below 1 molar nitrate, see Figure 1. Current controls on the tank farm solution chemistry are in place to prevent the initiation and propagation of pitting and stress corrosion cracking in the primary steel waste tanks. The controls are based upon a series of experiments performed with simulated solutions on materials used for construction of the tanks, namely ASTM A537 carbon steel (A537). During FY09, an experimental program was undertaken to investigate the risk associated with reducing the minimum molar nitrite concentration required to confidently inhibit pitting in dilute solutions (i.e., less than 1 molar nitrate). The experimental results and conclusions herein provide a statistical basis to quantify the probability of pitting for the tank wall exposed to various solutions with dilute concentrations of nitrate and nitrite. Understanding the probability for pitting will allow the facility to make tank-specific risk-based decisions for chemistry control. Based on previous electrochemical testing, a statistical test matrix was developed to refine and solidify the application of the statistical mixture/amount model to corrosion of A537 steel. A mixture/amount model was identified based on statistical analysis of recent and historically collected electrochemical data. This model provides a more complex relationship between the nitrate and nitrite concentrations and the probability of pitting than is represented by the model underlying the current chemistry control program, and its use may provide a technical basis for the utilization of less nitrite to inhibit pitting at concentrations below 1 molar nitrate. FY09 results fit within the mixture/amount model, and further refine the nitrate regime in which the model is applicable. The combination of visual observations and cyclic potentiodynamic polarization scans indicates a potential for significant inhibitor reductions at nitrate concentrations near 1.0 M without a significant increase in corrosion risk. The complete data sets from FY08 and FY09 testing have determined the statistical basis to confidently inhibit against pitting using nitrite inhibition with the current pH controls. Future testing will complete the spectrum of nitrate concentrations around 1 molar. These results will be combined to provide a complete spectrum for corrosion controls with a risk based component.

[发布日期] 2010-12-09

[学科分类] 材料科学（综合）

[关键词] CARBON STEELS;CHEMISTRY;CONSTRUCTION;CORROSION;NITRATES;NITRITES;POLARIZATION;PROBABILITY;STEELS;STORAGE FACILITIES;STRESS CORROSION;TANKS;TESTING;WASTES