Analysis of Monolith Cores from an Engineering Scale Demonstration of a Prospective Cast Stone Process

[摘要] The primary disposition path of Low Activity Waste (LAW) at the DOE Hanford Site is vitrification. A cementitious waste form is one of the alternatives being considered for the supplemental immobilization of the LAW that will not be treated by the primary vitrification facility. Washington River Protection Solutions (WRPS) has been directed to generate and collect data on cementitious or pozzolanic waste forms such as Cast Stone. This report documents the coring and leach testing of monolithic samples cored from an engineering-scale demonstration (ES Demo) with non-radioactive simulants. The ES Demo was performed at SRNL in October of 2013 using the Scaled Continuous Processing Facility (SCPF) to fill an 8.5 ft. diameter x 3.25 ft. high container with simulated Cast Stone grout. The Cast Stone formulation was chosen from the previous screening tests. Legacy salt solution from previous Hanford salt waste testing was adjusted to correspond to the average LAW composition generated from the Hanford Tank Waste Operation Simulator (HTWOS). The dry blend materials, ordinary portland cement (OPC), Class F fly ash, and ground granulated blast furnace slag (GGBFS or BFS), were obtained from Lafarge North America in Pasco, WA. In 2014 core samples originally obtained approximately six months after filling the ES Demo were tested along with bench scale molded samples that were collected during the original pour. A latter set of core samples were obtained in late March of 2015, eighteen months after completion of the original ES Demo. Core samples were obtained using a 2??? diameter x 11??? long coring bit. The ES Demo was sampled in three different regions consisting of an outer ring, a middle ring and an inner core zone. Cores from these three lateral zones were further segregated into upper, middle and lower vertical segments. Monolithic core samples were tested using the Environmental Protection Agency (EPA) Method 1315, which is designed to provide mass transfer rates (release rates) of inorganic analytes contained in monolithic material under diffusion controlled release conditions as a function of leaching time. Compressive strength measurements and drying tests were also performed on the 2015 samples. Leachability indices reported are based on analyte concentrations determined from dissolution of the dried samples.

[发布日期] 2016-06-01

[学科分类] 核能源与工程

[关键词] WASTE FORMS;FLY ASH;PORTLAND CEMENT;LEACHING;TANKS;COMPRESSION STRENGTH;CONCENTRATION RATIO;SALTS;TESTING;MASS TRANSFER;DRYING;TIME DEPENDENCE;GROUTING;SIMULATIO