Mechanical properties of polymer-modified porous concrete

[摘要] In this research work, polymer-modified porous concretes (permeable concretes) using polymer latex and redispersible polymer powder with water-cement ratio of 30 %, polymer-cement ratios of 0 to 10 % and cement content of 300 kg/m3are prepared. The porous concrete was tested for compressive strength, flexural strength, water permeability and void ratio. The cubes size of specimen is 100 mm 100 mm 100 mm and 150 mm 150 mm 150 mm while the beam size is 100 mm 100 mm 500 mm was prepared for particular tests. The tests results show that the addition of polymer as a binder to porous concrete gives an improvement on the strength properties and coefficient of water permeability of polymer-modified porous concrete. It is concluded from the test results that increase in compressive and flexural strengths and decrease in the coefficient of water permeability of the polymer-modified porous concrete are clearly observed with increasing of polymer-cement ratio.

[发布机构] Faculty of Civil Engineering and Earth Resources, Universiti Malaysia Pahang, Lebuhraya Tun Razak, Pahang Gambang; 26300, Malaysia^1;Department of Structure and Material, Faculty of Civil Engineering, Universiti Teknologi Malaysia, Johor; 81310, Malaysia^2;Department of Civil Engineering, Faculty of Applied Sciences, University of British Columbia, Vancouver; BC; V6T 1Z4, Canada^3

[效力级别] 自然科学

[关键词] Addition of polymer;Compressive and flexural strengths;Mechanical properties of polymers;Permeable concretes;Polymer-cement ratio;Redispersible polymer powder;Water permeability;Water-cement ratio