The effect of salivary pH on diametral tensile strength of resin modified glass ionomer cement coated with coating agent

[摘要] The aim of this study was to evaluate the effect of artificial saliva with different acidities on the diametral tensile strength of Resin Modified Glass Ionomer Cement (RMGIC) coated with varnish and nanofilled coating agent. The specimens coated with coating agents were immersed in artificial saliva with pH of 4.5, 5.5, and 7 for 24 hours in an incubatorat 37°C. The diametral tensile strength of the specimens was tested with Universal Testing Machine. There were no significant differences on the diametral tensile strength of all specimens that were put into groups based on the acidity of the saliva and the type of coating agent (p>0.05). Both varnish and nanofilled coating agent stayed on the RMGIC in the acidic condition that simulated the true condition of oral cavity in people with high caries risk for the 24 hours of maturation.

[发布机构] Department of Dental Materials, Faculty of Dentistry, Universitas Indonesia, Jakarta, Indonesia^1

[效力级别] 医药卫生 [学科分类] 卫生学

[关键词] Acidic conditions;Artificial saliva;Coating agents;Diametral tensile strength;Oral cavity;Resin-modified glass-ionomer cement;Universal testing machines