Improved understanding of the dynamic response in anisotropic directional composite materials through the combination of experiments and modeling

[摘要] Recently there has been renewed interest in the dynamic response of composite materials; specifically low density epoxy matrix binders strengthened with continuous reinforcing fibers. This is in part due to the widespread use of carbon fiber composites in military, commercial, industrial, and aerospace applications. The design community requires better understanding of these materials in order to make full use of their unique properties. Planar impact testing was performed resulting in pressures up to 15 GPa on a unidirectional carbon fiber - epoxy composite, engineered to have high uniformity and low porosity. Results illustrate the anisotropic nature of the response under shock loading. Along the fiber direction, a two-wave structure similar to typical elastic-plastic response is observed, however, when shocked transverse to the fibers, only a single bulk shock wave is detected. At higher pressures, the epoxy matrix dissociates resulting in a loss of anisotropy. Greater understanding of the mechanisms responsible for the observed response has been achieved through numerical modeling of the system at the micromechanical level using the CTH hydrocode. From the simulation results it is evident that the observed two-wave structure in the longitudinal fiber direction is the result of a fast moving elastic precursor wave traveling in the carbon fibers ahead of the bulk response in the epoxy resin. Similarly, in the transverse direction, results show a collapse of the resin component consistent with the experimental observation of a single shock wave traveling at speeds associated with bulk carbon. Experimental and simulation results will be discussed and used to show where additional mechanisms, not fully described by the currently used models, are present.

[发布机构] Sandia National Laboratories, PO Box 5800 MS-1195, Albuquerque; NM; 87185, United States^1;HI-TEST Laboratories, Applied Technologies Group, PO Box 87, Arvonia; VA; 23004, United States^2

[关键词] Carbon fiber composite;Carbon fiber epoxy composites;Design community;Elastic-plastic response;Longitudinal fibers;Micro-mechanical;Reinforcing fibers;Resin components