Presented in the first part of this thesis is work performed on the ionizing energy beam induced adhesion enhancement of thin (~ 500 Angstrom) Au films on GaAs substrates. The ionizing beam, employed in the present thesis, is the MeV ions (i.e., 16O, 19F, and 35Cl), with energies between 1 and 20 MeV. Using the "Scratch" test for adhesion measurement, and ESCA for chemical analysis of the film-substrate interface, the native oxide layer at the interface is shown to play an important role in the adhesion enhancement by the ionizing radiation. A model is discussed which explains the experimental data on the the dependence of adhesion enhancement on the energy which was deposited into electronic processes at the interface. The ESCA data indicate that the chemical bonds (or compounds), which are responsible for the increase in the thin film adherence, are hydroxides rather than oxides.
In the second part of the thesis we present a research performed on the radiation damage in GaAs crystals produced by MeV ions. Lattice parameter dilatation in the surface layers of the GaAs crystals becomes saturated after a high dose bombardment at room temperature. The strain produced by nuclear collisions is shown to relax partially due to electronic excitation (with a functional dependence on the nuclear and electronic stopping power of bombarding ions). Data on the GaAs and GaP crystals suggest that low temperature recovery stage defects produce major crystal distortion. The x-ray rocking curve technique with a dynamical diffraction theory analysis provides the depth distribution of the strain and damage in the MeV ion bombarded crystals.