Raman Spectroscopy, X-Ray, SEM, and DTA Analysis ofAlkali-Phosphate Glasses ContainingWO3and Nb2O5

[摘要] New phosphate glasses in the quaternary system (50-x) A2O-xWO3-10 Nb2O5-40 P2O5, withx= 0; 30 and A = Li or Na were prepared by the melt quenching method. The effect on the crystallization behaviour of the glass due to the introduction of WO3into the glass composition and, consequently, the diminishing of the molar amount of the alkaline oxide and the decreasing of the molar ratio between network modifiers and network formers (M/F) was studied. The prepared glasses were heat-treated in air, at 550°C, 600°C, and 650°C for 4 hours. The structure, of the obtained samples, was studied by differential thermal analysis (DTA), X-ray powder diffraction (XRD), and Raman spectroscopy and the morphology by scanning electron microscopy (SEM). It was found that the replacement of Li2O or Na2O by WO3reduces the number of the crystallised phases. In the lithium-niobiophosphate glasses, the presence of WO3promotes the formation of NbOPO4instead of the LiNbO3phase and reduces the formation of ortho- and pyro-phosphate phases. The thermal treatments affect the arrangements of the network structure of the AW40-glasses.

[学科分类] 光谱学