Photo- and Electrochromic Properties of Activated Reactive EvaporatedMoO3Thin Films Grown on Flexible Substrates

[摘要] The molybdenum trioxide (MoO3) thin films were grown onto1×10−3Torr, respectively. The influence of substrate temperature on the microstructural and optical properties was investigated. TheMoO3thin films prepared at a substrate temperature of 523 K were found to be composed of uniformly distributed nanosized grains with an orthorhombic structure ofα-MoO3. These nanocrystallineMoO3thin films exhibited higher optical transmittance of about 80% in the visible region with an evaluated optical band gap of 3.29 eV. With the insertion of 12.5 mC/cm2, the films exhibited an optical modulation of 40% in the visible region with coloration efficiency of 22 cm2/C at the wavelength of 550 nm. TheMoO3films deposited at 523 K demonstrated better photochromic properties and showed highest color center concentration for the irradiation time of 30 minutes at 100 mW/cm2.

[学科分类] 材料工程