Analysis on the Behavior of Nonpropagating Fatigue Cracks under Steep Stress Gradients

[摘要] A mechanism for the formation of nonpropagating fatigue cracks ahead of a notch root is presented. The stress gradients near the elongated notch root along with the propagation of short crack and the resulting nonpropagating crack lengthsanpcare estimated. The local stress which is higher than the unnotched material fatigue limitS0initiates the crack from a notch root and local steep stress gradient as a very important element leads to the nonpropagating crack. The value ofanpcdepends on the material properties, and specimen geometry as well as applied loading. The characteristic size of the short cracka0which depends on the material properties associates with the fatigue stress concentration factorKf. The estimated values ofanpcare in fairly good agreement with the experimental values available.