Thermomechanical Behavior of High Performance Epoxy/Organoclay Nanocomposites

[摘要] Nanocomposites of epoxy resin containing bentonite clay were fabricated to evaluate the thermomechanical behavior during heating. The epoxy resin system studied was prepared using bifunctional diglycidyl ether of bisphenol A (DGEBA), crosslinking agent diaminodiphenylsulfone (DDS), and diethylenetriamine (DETA). The purified bentonite organoclay (APOC) was used in all experiments. The formation of nanocomposite was confirmed by X-ray diffraction analysis. Specimens of the fabricated nanocomposites were characterized by dynamic mechanical analysis (DMA). According to the DMA results a significant increase in glass transition temperature and storage modulus was evidenced when 1 phr of clay is added to epoxy resin.

[学科分类] 材料工程