The Studies of the Water-Vapour Transmission Rate and It's Proofness on the Various Commercial Polymer Films

[摘要] The water-vapour transmission ratios (WVTR) of the various commercial polymer films have been investigated at the constant pressure and relative humidity (RH). Water proofnesses, the reciprocals of WVTR for the various samples, were determined using a cup device and maintaining the sample films at a constant temperature (40¡¾1¡É) and a constant R. H (90¡¾2%) for 24 hours. The following order of the relative proofness was observed; oriented polypropyrene (O.PP) > high density polyethylene (HDPE, Inflation) > high density polyethylene (HDPE. T-die) > casted polypropylene (C. PP) > nonoriented polyester (N. PET) > low density polyethylene (LDPE) > oriented polyester (O. PET) > rigid polyvinyl chloride (Rigid PVC) > semirigid polyvinyl chloride (Semirigid PVC) > nonrigid polyvinyl chloride (Nonrigid PVC) > oriented nylon (O. Nylon) > nonoriented nylon (N. Nylon). And water proofness order was also observed to decrease with the temperature rising; HDPE (T-die) > C. PP > O. PET > LDPE > O. Nylon. The activation energies of LDPE, HDPE (T-die), C. PP, O. PET and O.Nylon films were 12.0, 11.1, 11.4, 11.7, 14.1 kcal/mole, respectively. The WVTR's of the films were increased with the polarity of polymer and the addition of plasticizer in PVC, decreased with the increase of the film thickness and mechanical orientation. The WVTR's of the laminated films O. PP/LDPE, N.Nylon/LDPE, C.PP/LDPE were also more dependent on the film thickness than the WVTR's of the single films.

[学科分类] 化学（综合）