Dependences on Heating Conditions and Applicabilities as an Additive for ECIA of Sr1-xBaxFe3+ 1- ¥óFe4+ ¥óO3-y Ferrite System
[摘要] The solid solutions of the Sr1-xBaxFeO3-y system (x = 0.0, 0.1, 0.2 and 0.3) having a perovskite structure were prepared in air at 1423 K and then heat-treated in air (A), O2(O) and N2(N) to examine possibility of controlling the nonstoichiometry and applicability as an additive for electrical conducting inorganic adhesives (ECIA). In the samples heated in N2 stream, there existed almost no Fe4+ ions, and at constant temperature their electrical conductivities were considerably lower than those of the samples heat-treated in air or O2. Sr0.8Ba0.2Fe3+ 0.49Fe4+ 0.51O2.76 (SB2-A) whose Fe3+/Fe4+ ratio was nearly 1 (0.96) and whose conductivity values (1.04 ohm?1cm?1 at 283 K and 1.88 ohm?1cm?1 at 673 K) were higher than any other samples, was found to be the best additive for ECIA.
[发布日期] [发布机构]
[效力级别] [学科分类] 化学（综合）
[关键词] Solid solution;Heat-treated;Electrical conducting inorganic adhesives;Electrical conductivity;Nonstoichiometry [时效性]