Oxidation behaviour of the near α-titanium alloy IMI 834

[摘要] Oxidation behaviour of the near ð›�?-titanium alloy IMI 834 was investigated over a range of temperatures, from 600â€�??800°C, in air. Specimens were solution-treated in the ð›�? + ð›�? and ð›�? phase fields for 1 h and 1/2 h, respectively and cooled in air to room temperature. The solution treated samples were subjected to stabilization treatment at 700°C for 2 h, followed by cooling in air. Oxidation behaviour of these samples was studied from 600â€�??800°C in air, for 50 h. The morphology of the scales formed was examined by SEM and the phases present in the scales were characterized by X-ray diffraction. While there was little oxidation at 600°C, the rate of oxidation increased at higher temperatures. In general, the rate of oxidation was found to be more in the ð›�? + ð›�? treated condition than that in the ð›�? treated one. The results are discussed in terms of the characteristics of the oxide film formed under different conditions.

[学科分类] 材料工程

[关键词] Near ð›�?-titanium alloy IMI 834;thermogravimetric studies;activation energy;oxidation behaviour;surface morphology.