Proton induced modification in makrofol-DE

[摘要] Irradiation effects of a 3 MeV proton beam on polycarbonate (makrofol-DE (MFD)) have been studied with respect to its electrical, thermal and structural behaviour by using an LCR meter, DSC/TGA and FTIR spectroscopy. The dielectric loss/constant was observed to change with the fluence. Thermal analysis revealed that chain scission is the dominant phenomena in irradiated samples based on the reduction of its thermal stability by about 19% at a fluence of 10¹⁵ ions/cm², which is also corroborated by FTIR spectra. No significant change in intensity of the absorbance bands of the irradiated sample was observed up to a fluence of 10¹⁴ ions/cm² while on increasing fluence (10¹⁵ ions/cm²) the polymer structure was modified. It appears from DSC thermograms that ð‘�??_g is observed to change with fluence.

[学科分类] 材料工程

[关键词] Makrofol-DE;FTIR;DSC;TGA;a.c. electrical frequency.