Ultra low and negative expansion glass�?�ceramic materials produced from pyrophyllite and blast furnace slag

[摘要] Ultra low and negative expansion glassâ€�?�ceramic materials have been obtained from pyrophyllite and blast furnace slag. The batch composition was modified with the addition of lithium carbonate, hydrated alumina, boric acid and nucleating agent (titania). The batch was melted at 1400°C followed by casting in the form of bars and annealed at 510°C for 4 h. The annealed specimens were subjected to heat treatment at predetermined temperatures selected from DTA study of the parent glass. Thermal expansion measurement and X-ray diffraction analysis revealed that the specimen nucleated at 545°C for 4 h and crystallized at 720°C for 2 h which resulted in negative coefficient of thermal expansion [(â€�??) 9 to (â€�??) 2 Ã�? 10$^{-7}/{}^circ $C] over the temperature range (30â€�??600°C) due to the formation of ð›�?-eucryptite while other heating schedule showed the formation of spodumene and lithium aluminium silicates. The samples showed excellent flexural strength value and varied in the range 120â€�??200 MPa depending upon the phases present.

[学科分类] 材料工程

[关键词] Glassâ€�?�ceramic;Li2Oâ€�?�Al2O3â€�?�SiO2;blast furnace slag;pyrophyllite.