Synthesis of nanocrystalline materials through reverse micelles: A versatile methodology for synthesis of complex metal oxides

[摘要] We have been successful in obtaining monophasic nanosized oxides with varying chemical compositions using the reverse micellar method. Here we describe our methodology to obtain important metal oxides like ceria, zirconia and zinc oxide. The oxalate of cerium, zirconium and zinc were synthesized using the reverse micellar route. While nanorods of zinc oxalate with dimension, 120 nm in diameter and 600 nm in length, could be obtained, whereas spherical particles of size, 4â€�??6 nm, were obtained for cerium oxalate. These precursors were heated to form their respective oxides. Mixture of nanorods and nanoparticles of cerium oxide was obtained. ZrO₂ nanoparticles of 3â€�??4 nm size were obtained by the thermal decomposition of zirconium oxalate precursor. ZnO nanoparticles (55 nm) were obtained by the decomposition of zinc oxalate nanorods. Photoluminescence (PL) studies at 20 K shows the presence of three peaks corresponding to free excitonic emission, free to bound and donorâ€�?�acceptor transitions. We also synthesized nanoparticles corresponding to Ba_{1â€�?�ð�?��?}Pb_ð‘�?ZrO₃ using the reverse micellar route. The dielectric constant and loss were stable with frequency and temperature for the solid solution.

[学科分类] 材料工程

[关键词] Reverse micelles;nanorods;photoluminescence;dielectric properties.