Metal oxide/polyaniline nanocomposites: Cluster size and composition dependent structural and magnetic properties

[摘要] Nanocomposites of iron oxide with conducting polymer in the form of powders of varying compositions have been studied to understand the effects of particle size, cluster size and magnetic inter-particle interactions. The sizes of the nanoparticles were estimated to be ∼ 10â€�??20 nm from the X-ray diffraction (XRD) and the transmission electron micrographs (TEM). XRD shows a single crystalline phase for the ð›�?-Fe₂O₃. The presence of conducting polymer was confirmed through Fourier transform infrared (FTIR) spectroscopy. The amount of polymer present in the composite, the transition temperature of iron oxide and the thermal stability of polymer was determined through thermogravimetric and differential thermal analysis (TGAâ€�?�DTA). The room temperature magnetic hysteresis measurements show reduction in saturation magnetization with increasing polymer concentrations. A low value of coercivity was observed for low polymer composites. On increasing the polymer concentration, the coercivity and remanence become negligible indicating a superparamagnetic phase at room temperature. Beyond a certain composition, the system shows paramagnetic behaviour which is also confirmed through zero field cooledâ€�?�field cooled (ZFCâ€�?�FC) measurements. We also report preliminary results on the magnetic properties of self standing sheets prepared using ð›�?-Fe₂O₃ and NiFe₂O₄ nanoparticles and conducting polymers.

[学科分类] 材料工程

[关键词] Metal oxide/polyaniline nanocomposites;structural properties;magnetic properties.