Fine structure at the diffusion welded interface of Fe3Al/Q235 dissimilar materials

[摘要] The interface of Fe₃Al/Q235 dissimilar materials joint, which was made by vacuum diffusion welding, combines excellently. There are Fe₃Al, FeAl phases and ð›�?-Fe (Al) solid solution at the interface of Fe₃Al/Q235. Aluminum content decreases from 28% to 1.5% and corresponding phase changes from Fe₃Al with DO₃ type body centred cubic (bcc) structure to ð›�?-Fe (Al) solid solution with B2 type bcc structure. All phases are present in sub-grain structure level and there is no obvious brittle phases or micro-defects such as pores and cracks at the interface of Fe₃Al/Q235 diffusion joint.

[学科分类] 材料工程

[关键词] Fe3Al/Q235 dissimilar material joint;vacuum diffusion welding;fine structure.