The durability of natural sisal fibre reinforced cement-based composites

[摘要] ENGLISH ABSTRACT: The building industry is responsible for a substantial contribution to pollution. The production of building materials, as well as the operation and maintenance of structures leads to large amounts of carbon-dioxide (CO2) being release in the atmosphere. The use of renewable resources and construction materials is just one of the ways in which the carbon footprint of the building industry can be reduced.Sisal fibre is one such renewable material. Sisal fibre is a natural fibre from the Agave Sisalana plant. The possibility of incorporating sisal fibre in a cement-based matrix to replace conventional steel and synthetic fibres has been brought to the attention of researchers. Sisal fibre has a high tensile strength in excess of polypropylene fibre and comparable to PVA fibre. Sisal fibre consists mainly of cellulose, hemi-cellulose and lignin. The disadvantage of incorporating sisal fibre in a cement-based matrix is the degradation of the composite. Sisal fibres tend to degrade in an alkaline environment due to changes in the morphology of the fibre. The pore water in a cement base matrix is highly alkaline which leads to the degradation of the fibres and reduced strength of the composite over time.Sisal fibre reinforced cement-based composites (SFRCC) were investigated to evaluate the durability of the composites. Two chemical treatments, alkaline treatment and acetylation, were performed on the fibre at different concentrations to improve the resistance of the fibre to alkaline attack. Alkaline treatment was performed by using sodium hydroxide (NaOH), while acetylation was performed by using acetic acid or acetic anhydride. Single fibre pull-out (SFP) tests were performed to evaluate the influence of chemical treatment on fibre strength, to study the fibre-matrix interaction and to determine a critical fibre length. A matrix consisting of ordinary Portland cement (OPC), sand and water were used for the SFP tests. This matrix, as well as alternative matrices containing fly ash (FA) and condensed silica fume (CSF) as supplementary cementitious material, were reinforced with 1% sisal fibre (by volume) cut to a length of 20 mm. The OPC matrix was reinforced with untreated- and treated fibre while the alternative matrices were reinforced with untreated fibre. Alternative matrices containing varying fibre volumes and lengths were also produced. Three-point bending- (indirect), direct tensile- and compression tests were performed on specimens at an age of 28 days to determine the strength of the matrix. The remainder of the specimens were subjected to ageing by extended curing in water at 24˚C and 70˚C respectively and by alternate cycles of wetting and drying, after which it was tested at an age of 90 days from production to evaluate the durability of the fibre. An increase in fibre volume led to a decrease in compressive strength and peak tensile strength. The optimum fibre length at a volume of 1% was 20 mm for which the highest compression strength was recorded. The combination of alkali treatment and acetylation was the most effective treatment condition, followed by alkali treatment at low concentrations of sodium hydroxide. At higher concentrations of sodium hydroxide, a significant reduction in strength was recorded. The addition of supplementary cementitious materials also proved to be effective in mitigating degradation, especially in the cases where CSF was used. FA proved to be less effective in reducing the alkalinity of the matrix. However, the use of FA as fine filler resulted in higher strengths. Specimens manufactured by extrusion did not have superior mechanical properties to cast specimens.The conclusion was made that the use of sisal fibre in a cement-based matrix is effective in providing ductile failure. Chemical treatment and the addition of supplementary cementitious materials did improve the durability of the specimens, although degradation still took place.

[发布机构] Stellenbosch University