Ge0.57Ti0.43O2: a new high-pressure material with rutile-type crystal structure

[摘要] Single crystals of a GeO2–TiO2 solid solution with the corresponding composition Ge0.57Ti0.43O2 (germanium titanium tetra­oxide) were obtained by devitrification of germania-titania glass at high pressure and temperature. The new compound crystallizes in the rutile structure type (space group P42/mnm), where Ge and Ti share the same position M (site symmetry m.mm), with occupancy values of 0.57 (3) and 0.43 (3), respectively, and one O-atom position (m.2m). The M site is in a sixfold O-atom coordination and, as in the original TiO2 rutile structure, an elongation of the O—M—O bonds along the c-axis direction of the coordination polyhedron and deviation of the angles from 90° lead to a decrease in the coordination symmetry from octa­hedral to tetra­gonal. The Ge and Ti atoms are fully disordered in the structure, which indicates that the rutile structure is surprisingly pliant given the differing sizes of the two cations.

[学科分类] 数学（综合）

[关键词] TITANIA-GERMANIA;SOLID SOLUTION;RUTILE STRUCTURE;HIGH PRESSURE;HIGH TEMPERATURE;CRYSTAL STRUCTURE