Effect of Fiber Post-Resin Matrix Composition on Bond Strength of Post-Cement Interface

[摘要] Objective. To evaluate the influence of 3 different post-resin matrix systems cemented with dual-cure resin cement in simulated root canals made of PMMA acrylic sheet. Methods. 3 types of fiber posts (n = 60) with different resin matrixes divided into 3 groups group 1 cross-linked FRC Postec Plus post (n = 20), group 2 cross-linked Rely X post (n = 20), and group 3 Interpenetrated IPN Everstick post (n = 20). All posts were cemented using Multilink Automix dual-cure cement. Posts were cemented into acrylic blocks in order to purely test the strength of cement-post interface. After one week storage at 37°C, two sections of 1 mm thickness from middle-third were subjected to micro-push-out test at crosshead speed 0.5 mm/min. Results. The data were analyzed using one-way analysis of variance (ANOVA). The variable fiber post-matrix system was found to significantly affect the push-out bond strength (). Group 2 exhibited that the highest mean push-out bond strength was (5.36

[学科分类] 口腔科学