Synthesis of Ni/Graphene Nanosheets via Electron Beam Irradiation and Their Enhanced Electrochemical Hydrogen Storage Properties

[摘要] A nanostructured Ni(OH)2/graphene oxide (GO) hybrid was fabricated via the controlled reassembly of exfoliated GO with nickel hydroxide to form a delaminated structure. To examine the effect of electron beam irradiation on the hybrid material, the obtained Ni(OH)2/GO was exposed to the electron beam, and the total doses of the electron beam were varied from 150 to 250 kGy. The electron‐beam‐irradiated hybrid was reduced to fabricate a new nanostructured material in which nickel nanoparticles were homogeneously deposited onto the graphene nanosheets (GNS). According to the transmission electron microscopy analysis, a large number of defect sites could be developed after the electron beam treatments. The electrochemical hydrogen storage property (approximately 170 mAh/g) of the hybrid sample after the electron beam treatment was determined to be much superior to that of the GNS (approximately 20 mAh/g), demonstrating that this synthetic methodology via electron beam bombardment could be extended to the development of new nanostructured materials with enhanced hydrogen storage properties.

[学科分类] 化学（综合）

[关键词] Exfoliation;Graphene nanosheet;Electron beam irradiation;Hydrogen storage