Preparation and characterization of Eu3+ activated CaSiO3, (CaA)SiO3 [A = Ba or Sr] phosphors

[摘要] Eu3+ activated CaSiO3, (Ca, Ba) SiO3 and (Ca, Sr) SiO3 have been prepared by sol–gel technique. Residual solvent and organic contents in the gel were removed by firing at 100°C for 3–4 h at 300 and 600°C for 2 h. Small exothermic shoulder around 850 to 875°C, as observed in DTA curve, corresponds to crystallization temperature of the doped calcium silicate. Influence of firing temperature on the luminescence of Eu3+ shows the maximum emission intensity in gel fired at 850°C. Photoluminescence emission peak is observed at 614 nm due to ${}^{5}D_{0} \rightarrow {}^{7}F_{2}$ transition of Eu3+ ion in (Ca, Ba) SiO3 and (Ca, Sr) SiO3 phosphors, when excited by 254 nm. The (Ca, Ba) SiO3 material is proposed as an efficient red phosphor.

[学科分类] 材料工程

[关键词] CaSiO3;photoluminescence;sol–gel;phosphor.