Alumina-Forming Austenitics: A New Approach to Thermal and Degradation Resistant Stainless Steels for Industrial Use

[摘要] A series of developmental AFA alloys was selected for study based on: 25 Ni wt.% (alloys A-F), 20 wt% Ni (alloys G-H), and 12 Ni wt.% (alloys I-L). An emphasis in this work was placed on the lower alloy content direction for AFA alloys to reduce alloy raw material cost, rather than more highly alloyed and costly AFA alloys for higher temperature performance. Alloys A-D explored the effects of Al (3-4 wt.%) and C (0.05-0.2 wt.%) in the Fe-25Ni-14Cr-2Mn-2Mo-1W-1Nb wt.% base range; alloys E and F explored the effects of removing costly Mo and W additions in a Fe-25Ni-14Cr-4Al-2.5Nb-2Mn-0.2C base, alloys G and H examined Nb (1-2.5wt.%) and removal of Mo, W in a Fe-20Ni-14Cr-3Al-2Mn-0.2 C wt.% base; and alloys I-L examined effects of C (0.1-0.2 wt.%) and Mn (5-10 wt.%) on a low cost Fe-14Cr-12Ni-3Cu-2.5Al wt.% base (no Mo, W additions). Creep testing resulted in elemental trends that included the beneficial effect of higher carbon and lower niobium in 20-25%Ni AFA alloys and, the beneficial of lower Mn in 12%Ni AFA alloys. Corrosion tests in steam and sulfidation-oxidation environments showed, in general, these alloys were capable of a ten-fold improvement in performance when compared to conventional austenitic stainless steels. Also, corrosion test results in metal-dusting environments were promising and, warrant further investigation.

[发布日期] 2012-05-31

[学科分类] 材料科学（综合）

[关键词] ALLOYS;CARBON;CORROSION;CREEP;NIOBIUM;PERFORMANCE;RAW MATERIALS;REMOVAL;STAINLESS STEELS;STEAM;TESTING corrosion;creep;alumina;steel;high temperature